6063 Aluminum Sheet

What Is The 6063 Aluminum Sheet

6063 alloy aluminum plate is softer than 6061 alloy aluminum sheet. It has many magnesium and silicon alloy characteristics. It has the excellent characteristics of good processing performance, excellent welding characteristics and electroplating, good corrosion resistance, high toughness, no deformation after processing, dense material, no defects and easy polishing, easy coloring film, good oxygenation effect and so on.

Aluminium 6063 Price Per Kg

6063 Aluminum Sheet Features:

Heat treatment strengthened, high impact toughness, insensitive to defects.
It has excellent thermoplasticity, can be extruded into a high-speed and complex structure, has a wide quenching temperature range and low quenching sensitivity.
Excellent welding performance and corrosion resistance, no tendency of stress corrosion cracking. Al-Mg-Si alloy is the only alloy that does not find stress corrosion cracking in heat-treated reinforced aluminum alloys.
After treatment, the surface of 6061 aluminum sheet is very smooth, easy to anodize and color. The disadvantage is that storage after quenching at room temperature for a period of time will negatively affect the strength (parking effect)

6063 Aluminum Sheet Mainly Tempers:

6063-O

Un-heat-treated 6063 has maximum tensile strength no more than 130 MPa (19,000 psi), and no specified maximum yield strength. The material has elongation (stretch before ultimate failure) of 18%.
6063-T1

T1 temper 6063 has an ultimate tensile strength of at least 120 MPa (17,000 psi) in thicknesses up to 12.7 mm (0.5 in), and 110 MPa (16,000 psi) from 13 to 25 mm (0.5 to 1 in) thick, and yield strength of at least 62 MPa (9,000 psi) in thickness up to 13 millimetres (0.5 in) and 55 MPa (8,000 psi) from 13 mm (0.5 in) thick. It has elongation of 12%.
6063-T4/6063-T5

T5 temper 6063 has an ultimate tensile strength of at least 140 MPa (20,000 psi) in thicknesses up to 13 millimetres (0.5 in), and 130 MPa (19,000 psi) from 13 mm (0.5 in) thick, and yield strength of at least 97 MPa (14,000 psi) up to 13 millimetres (0.5 in) and 90 MPa (13,000 psi) from13 to 25 mm (0.5 to 1 in). It has elongation of 8%.
6063-T6

T6 temper 6063 has an ultimate tensile strength of at least 190 MPa (28,000 psi) and yield strength of at least 160 MPa (23,000 psi). In thicknesses of 3.15 millimetres (0.124 in) or less, it has elongation of 8% or more; in thicker sections, it has elongation of 10%.
Other tempers

6063 is also produced in tempers T52, T53, T54, T55, and T832, with various improved desired properties.

6063 Aluminium Alloy

6063 Aluminum Plate Chemical Composition:

Other

97.5%

– 99.35%

0.45

– 0.90%

0.20

– 0.60%

0.35%

0.10%

Max 0.05% Each;
Max 0.15% Total

6063 Aluminum Sheet Mechanical Properties:

	T52	T6
Density	0.098 lb/in3	0.098 lb/in3
Ultimate Tensile Strength	27 ksi	35 ksi
Yield Tensile Strength	21 ksi	31 ksi
Fatigue Strength	9.7 ksi	10 ksi
Shear Strength	15 ksi	22 ksi
Shear Modulus	3,700 ksi	3,770 ksi
Hardness Rockwell \| Brinell	B17 \| 60	B27 \| 65
Elongation at Break Percentage	12%	22%
Modulus of Elasticity	10,000 ksi	10,000 ksi
Poisson’s Ratio	0.33	0.33
Machinability Percentage	N/A	50%
Melting Point	1,140-1,210 °F	1,140-1,210 °F
Specific Heat	2.15 x 10^-1 BTU/lb-°F	2.15 x 10^-1 BTU/lb-°F
Thermal Conductivity	1,450 BTU-in/hr-ft^2-°F	1,390 BTU-in/hr-ft^2-°F
Electrical Conductivity	53% IACS	53% IACS

Wholesale 6063 Aluminium Sheet

6063 Aluminum Plate Sizes Information:

Thickness:	0.1-600mm
Width:	100-3000m
Length:	500-16000mm
Temper:	O, T3, T4, T5, T6, T651, T451, T42, T62, etc.
Standard:	GB/T3880, GJB1541, GB/N167, JB2053, GJB2662, ASTM B209, ASME SB-209, EN 485, BS EN 573

6063 Aluminum Sheet Application

6063 aluminum sheet is widely used because of its good plasticity and very smooth surface for anodizing.
6063 aluminum alloy is widely used in the construction of aluminum doors, windows and curtain walls, irrigation pipes, vehicles, benches, furniture, elevators, electronic components, and various durable consumer goods. It is a common aluminum alloy model.